The Effect of Electroplating Time on Microstructural Properties and Hardness of Silver Coating on C10100 Alloy

الموضوعات : Journal of Environmental Friendly Materials

A. Taherkhani ¹ (Department of Materials Engineering, Central Tehran Branch, Islamic Azad University, Tehran, Iran)
Y. Shajari ² (Institute of Materials and Energy, Meshkin Dasht, Karaj, Iran)
K. Mirzavand ³ (Department of Metallurgy and Materials Engineering, Imam Khomeini International University, Qazvin, Iran)
A. Mellatkhah ⁴ (Department of Metallurgy and Materials Engineering, Ferdowsi University of Mashhad, Mashhad, Iran)
Z. S. Seyedraoufi ⁵ (Department of Materials Engineering, Karaj Branch, Islamic Azad University, Karaj, Iran)

تاريخ الإرسال : 17 الأربعاء , رمضان, 1440 تاريخ التأكيد : 10 الإثنين , محرم, 1441 تاريخ الإصدار : 04 الأحد , ربيع الثاني, 1441

الکلمات المفتاحية:

ملخص المقالة :

In the present study, the effect of electroplating time on the intensity of flow and the constant potential difference on the thickness of the coating, surface smoothness, microstructure of the interface between substrate and coating and hardness of coating were investigated. Microstructural studies by optical microscopy (OM) showed that increasing the electroplating time leads to increase the coating thickness. Investigations showed that increasing the plating time due to growth leads to increase the surface roughness of coating. In the middle part of the coating, by increasing the time of plating, the thickness of eutectic Ag-Cu film increased. The results of microhardness of coatings showed that the maximum hardness was achieved at the highest planting time i.e 8 minutes. The microhardness remained at a constant range for about half a minute to two minutes, but increasing the time to 4 and 8 minutes leads to increase toughness of 107 and 131 Hv.

المصادر:

[1] M. Antler, Wear, 106,(1985), 5.

[2] J. S. Cho, K. A. Yoo, J. T. Moon, S. B. Son, S. H. Lee and K. H. Oh, Met. Mater. Int., 18, (2012), 881.

[3] S. L. Tay, Electrodeposition Coatings by Ionic Co-Discharge Technique. Ph.D. Thesis, University of Auckland, Auckland, New Zealand, (2016).

[4] R. Crisp, J. Rungis and J. K. Philos. Mag., (1970), 22, 217.

[5] Y. Wang, G. Cheng, L. Tay, Y. Guo, X. Sun and W. Gao, Mater., 10, (2017), 1.

[6] W. Xiao, Y. Lei, Z. Xia, X. Chen, Yu Han and J. Nie, J. Alloys Compd., Vol. 724, (2017), 24.

[7] K. M. S. Youssef, C. C. Koch and  P.S. Fedkiw, J. Electrochem. Soc. 151(C) (2004), 103.

[8] S. Berger and G. Hoffacker, Plat. Surf. Finish. 92 (2005), 46.

[9] M. Saitou and Y. Fukuoka, J. Electrochem. Soc. 151(C) (2004), 627.

[10] Surface Coating of Copper Alloy Strip for Electrical Connector Applications, Technical Inquiries, Materion Corporation, Materion Brush Performance Alloys, (2011).

[11] P. Gupta, R. K. Gupta, S. D. Chandran, P. K. Jayan and S. Gopinath, Mater., 5, 2018, 7496.

[12] O. Güler, T. Varol, Ü. Alver and A. Çanakçı, J. Alloys Compd., 782 (2019), 679.

[13] T. Török, A. Csik, J. Hakl, K. Vad, L. Kövér, J. Toth, S. Mészáros, E. Kun and D. Sós, Corros. Stud. Surf. Treat. 33, (2015), 1.

[14] C. Chang, Z. Lei, Y. Li and Z. Wang, J. The Electrochem. Soc.,163, 3 (2016), 121.

[15] H. Nawafune, K. Shiroguchi, S. Mizumoto, Y. Kohashi and K. Obata, J. Surf. Finish. Soc Jpn., 52, 10, (2001), 702.

[16] B. Vasconcelos, K. Vediappan, J. C. Oliveira and C. Fonseca, Appl. Surf. Sci., 443, (2018), 39.

[17] P. N. Reddy, M. H. P. Reddy, J. F. Pierson and S. Uthanna, Int. Scholarly Res. Not. (ISRN) Opt., (2014), 7 pages, Article ID: 684317.

[18] A. R. Rafieerad, A. R. Bushroa, B. Nasiri-Tabrizi, J. Vadivelu and W. J. Basirun, Surf. Coat. Technol. , 302, (2016), 275.