High efficient extraction of samarium (III) from aqueous solutions using 1, 10- phenanthroline-2, 9-dicarboxilic acid modified Fe3O4/GO nanosheets prior to determination by ICP-OES
الموضوعات : Journal of Nanoanalysis
Leila Farzin
1
(Radiation Application Research School, Nuclear Science and Technology Research Institute, P.O. Box 11365-3486, Tehran, Iran)
Mojtaba Amiri
2
(Radiation Application Research School, Nuclear Science and Technology Research Institute, P.O. Box 11365-3486, Tehran, Iran)
الکلمات المفتاحية: Samarium, ICP-OES, Magnetic Graphene Oxide,
ملخص المقالة :
There is a growing interest in the development of new methods for extraction of REEs from nuclear wastes. In this study, we fabricated a novel material composed of 1,10-phenanthroline-2,9-dicarboxilic acid (PDA) functionalized magnetic graphene oxide (Fe3O4/GO) for extraction of Sm(III) from aqueous solutions. Our interest in selection of carboxyl-containing ligand was due to its good coordination characteristic with Sm (III) which can be used to design a new sorbent. Under the optimized extraction conditions, the calibration graph for Sm (III) was linear in a concentration range of 6.2-784.5 µg L-1 with a correlation coefficient of 0.9900. A detection limit of 1.4 μg L−1 with an enrichment factor of 125 was obtained. Precisions, expressed as relative standard deviation for single-sorbent repeatability and sorbent-to-sorbent reproducibility, were 5.9% and 8.7% (n =5), respectively. Finally, spiked sea and river waters were analysed to evaluate the performance of the proposed method. The high recoveries (>%97) indicates that the suggested protocol is acceptable for determination of Sm (III) ions in the water samples.
Determination of samarium (III) ions in environmental samples after magnetic solid phase extraction using 1, 10- phenanthroline-2, 9-dicarboxilic acid modified Fe3O4/GO nanosheets
Leila Farzin* and Mojtaba Amiri
Radiation Application Research School, Nuclear Science and Technology Research Institute, P.O. Box 11365-3486, Tehran, Iran
Abstract
There is a growing interest in the development of new methods for extraction of REEs from nuclear wastes. In this study, we fabricated a novel material composed of 1,10-phenanthroline-2,9-dicarboxilic acid (PDA) functionalized magnetic graphene oxide (Fe3O4/GO) for extraction of Sm(III) from aqueous solutions. Our interest in selection of carboxyl-containing ligand was due to its good coordination characteristic with Sm (III) which can be used to design a new sorbent. Under the optimized extraction conditions, the calibration graph for Sm (III) was linear in a concentration range of 6.2-784.5 µg L-1 with a correlation coefficient of 0.9900. A detection limit of 1.4 μg L−1 with an enrichment factor of 125 was obtained. Precisions, expressed as relative standard deviation for single-sorbent repeatability and sorbent-to-sorbent reproducibility, were 5.9% and 8.7% (n =5), respectively. Finally, spiked sea and river waters were analysed to evaluate the performance of the proposed method. The high recoveries (>%97) indicates that the suggested protocol is acceptable for determination of Sm (III) ions in the water samples.
Keywords: ICP-OES; Magnetic graphene oxide; Samarium, Water samples
Introduction
Samarium (Sm) as a rare-earth element (REE) is of major interest for the development of several disciplines: coordination chemistry, organometallic compounds, luminescent compounds, catalysis and industrial applications. Rare-earth elements have found a variety of applications in nuclear and non-nuclear industries. These elements can enter human body via therapeutic and diagnostic agents (diagnostic and therapeutic radionuclides) and also contaminated air, food and drinking water as a result of industrial activities. Long-time exposure to REEs may exert a harmful influence on human liver, kidney, lung, and bone quality and result in some negative effects to immunologic system [1].
Each year, more than 10 thousand tons of spent fuels are discharged from nuclear power plants in the world [2]. Therefore, the proper management of spent fuels is a key issue for the sustainable development of nuclear energy. The isotope samarium-151 (151Sm) is a significant radionuclide in spent nuclear fuels, high-level radioactive wastes resulting from the processing of spent nuclear fuels and radioactive wastes associated with the operation of nuclear reactors and fuel reprocessing plants. This hazardoud radionuclide with a half-life of 90 years decays by emitting a relatively low-energy beta particle. This element is widely used in the nuclear reactors as controlling materials of neutron fluxes. In addition, 153Sm (1.9 days) has been suggested for treatment of painful metastatic bone disease [3]. So, an effective treatment method for determination of Sm (III) is strongly required. For this purpose, magnetic solid phase extraction (MSPE) is one of the most used methods for waste treatment due to simple operation, easy separation of the sorbent from matrix solution by the application of an external magnet, wide applicability and application in large scale [4]. Many kinds of sorbents such as activated carbons and biochars [5], seaweeds [6], ion imprinted polymers (IIP) [7], ion exchangers [8] and nanosorbents with the large surface area to volume ratio have been applied for treatment of Sm (III) contaminated wastewaters. Among these sorbents, carbon based nanomaterials especially graphene (G) and its derivatives have created noteworthy commercial interest their unique chemical and physical properties [9].
Graphene oxide (GO) is a new class of electron-rich carbon sorbents which shows promising applications in sample treatment. Fe3O4/GO nanocomposites combine the beneficial magnetic properties of the core and the possibility of binding to their surface [10, 11]. Some of the GO properties such as high surface area, ease of functionalization and good dispersibility due to the presence of the oxygen functionalities make it an ideal sorbent [4]. Despite the impressive properties of GO, direct application of GO as a selective and efficient adsorbent is still an insurmountable challenge [1]. In order to resolve the above problem, modification of inorganic or organic materials onto the GO sheets proves to be a feasible strategy. It is notable that the both sides of the planar sheets of graphene are available for modification with macromolecular ligands compared with fullerenes and carbon nanotubes (CNTs). In fact, a further incident that has attracted a great deal of interest towards GO is the advent of GO modification with various materials.
In recent years, the coordination chemistry of rare-earth cations with various carboxylic acids has attracted a lot of interest, due to the potential applications in many areas especially separation and extraction. According to the previous studies [12–14], it has been reported that carboxylic acids can act as excellent ligands for solvent extraction of lanthanides. The most important feature of the rare-earth carboxylate complexes is the large number of coordination types exhibited by these ligands, e.g, bidentate chelating, and bidentate bridging or tridentate chelatingbridging [15]. In the our previous study [16], a magnetic reduced GO decorated with thioglycolic acid (TGA)-capped CdTe quantum dots (QDs) was developed for SPE of cerium (Ce) ions from aqueous samples. The analytical potential of CdTe QDs in the extraction field was exploited through the manipulation of their surface chemistry by their capping with TGA, which improves their selective behaviour towards Ce (III) ions in samples of complex matrices. In the current work, we reported a 1, 10- phenanthroline-2, 9-dicarboxilic acid (PDA) modified Fe3O4/GO nanocomposite for MSPE of Sm (III) ions from aqueous samples prior to determination by inductively coupled plasma-optical emission spectroscopy (ICP-OES). This measurement technique suffers from interferences from the coexisting ions, especially some other lanthanides, Fe (III) and phosphate ions. Moreover, the problem is further complicated when the normal analytical concentrations are in the ultra-trace levels. Thus, a preconcentration step of Sm ions is recommended prior to its evaluation.
Experimental
Chemicals and reagents
All chemicals were of analytical grade purity and used as received. Natural graphite powder, hydrochloric acid (HCl, 37%), nitric acid (HNO3, 65%), acetic acid (CH3COOH, 100%), sulfuric acid (H2SO4, 98%), ethanol (C2H5OH, ≥99.8%), potassium permanganate (KMnO4, 99.9%), hydrogen peroxide (H2O2, 30%), ferric chloride hexahydrate (FeCl3.6H2O, 97%), ferrous chloride tetrahydrate (FeCl2.4H2O, 98%), ammonium hydroxide (NH4OH, 30%) and element standard solutions (1000 mg L-1) were purchased from Merck Company (Germany). 1, 10- phenanthroline-2, 9-dicarboxilic acid (PDA, C14H8N2O4) and ethylenediaminetetraacetic acid (EDTA, ≥98%) was supplied by Sigma Aldrich (USA).
Apparatus
Trace elements were determined by using a Perkin Elmer Optima 3100XL ICP-OES instrument (Shelton, CT, USA). Energy dispersive X-ray spectroscopy (EDX) analysis and FESEM studies was carried out by a Mira 3-XMU analytic microscope equipped with an energy dispersive X-ray analyzer. A 780 pH Meter was used for measuring pH at 25 °C (Metrohm, Switzerland). A sonoreactor UTR200 (Hielscher, Germany) with a maximum output power of 200 W, operating frequency of 24 kHz and ultrasonic intensity of 80 W cm-2 was employed for ultrasound-assisted exfoliation of graphite oxide.
Synthesis of Fe3O4/GO
The GO nanosheets were synthesized by oxidation and exfoliation of graphite powder based on the modified Hummer’s method [10]. In brief, 23 mL of concentrated sulphuric acid was added to the mixture of 1.0 g graphite flakes and 0.5 g sodium nitrate under constant stirring. After 1 h, 3.0 g KMnO4 was added to the above mixture gradually under stirring in an ice bath for 2 h to prevent overheating and explosion. Then, the mixture was placed in ultrasonic bath and irradiated for 2 h at 25 °C, and the resulting suspension was diluted by adding 500 mL of water under vigorous stirring. The resulting mixture was filtered and was washed three times with ultrapure water and 0.1 % HCl, respectively, and then dried at 60 °C for 12 h in a vacuum oven.
The magnetic graphene was synthesized by a chemical coprecipitation of iron ions according to the reported procedure by our group with slight modification [10]. In a similar experiment, 0.5 g GO was dispersed in 20 mL of deionized water using ultrasonic bath for 1 h. Subsequently, 0.43 g FeCl3.6H2O and 0.12 g FeCl2.4H2O were added to the GO suspension. The solution was heated up to 80 °C under nitrogen atmosphere with vigorous stirring (1000 rpm). Then, 1 mL of ammonia solution was quickly added to the mixture and the black precipitate was instantly formed. The mixture was allowed to stand for 5 min for complete precipitation. The precipitate was then collected using a magnet and the solution was decanted. The black precipitate was washed with double distilled water and was dried in vacuum at 65 °C.
Synthesis of PDA modified Fe3O4/GO
0.2 g of GO was ultrasonicated in 100 mL ethanol containing 0.1 g of 1, 10- phenanthroline-2, 9-dicarboxilic acid for 1 h and stirred at room temperature overnight. The resulting product was collected by filtration and washed several times with distilled water, then dried at 40 °C under a vacuum for 12 h.
Extraction procedure
To extraction of Sm, 60 mg of PDA modified Fe3O4/GO nanosheets were added into 50 mL of solution (pH 6), and shaken for 20 min at 35 °C. Then, the magnetic sorbent was collected at the bottom of the beaker by applying an external magnetic field via a super magnet (10 × 5 × 4 cm with a 1.4 Tesla magnetic field). The supernatant was separated by decantation and the magnet was removed. To desorption of analyte, 800 µL of HNO3-HCl-CH3COOH (40: 30: 30 %v/v) was added and the suspension was stirred for 12 min. Finally, the eluent was separated by magnetic decantation and analyzed using by ICP-OES for determination of elemental Sm.
Results and Discussion
Characterization of nanomaterials
Morphological studies
The morphologies of the (a) GO and (b) Fe3O4/GO nanocomposites were extensively characterized by FESEM (Fig. 1). The small Fe3O4 nanoparticles with an average size of about 30 nm (30±10 nm) decorate the surface of GO sheets. In addition, these images clearly shows transparent, regular and clear flakes of GO. But after modification with PDA (c), the surface of modified Fe3O4/GO nanocomposite becomes opaque, rough and irregular.
Fig. 1
EDX analysis
The functionalization of GO with PDA was supported by the elemental analysis. Fig. 2 shows the EDX spectra of Fe3O4/GO sorbent before (a) and after (b) binding with carboxylated ligand. The related spectra confirm the presence of this ligand on the surface of Fe3O4/GO as the nitrogen was found in the corresponding EDX. GO nanosheets were noncovalently functionalized with PDA through π-π interactions.
Fig. 2
Magnetic analysis
The magnetization hysteresis loop of GO/Fe3O4 and histidine functionalized GO/Fe3O4 nanocomposites was shown in Fig 3. The saturation magnetization of the GO/Fe3O4 found to be 59.8 emu/g, while the respective value of functionalized GO/Fe3O4 was smaller (46.7 emu/g). This can be attributed to the smaller percentage of magnetite in PDA modified GO/Fe3O4, due to the formation of functional groups on the surface of GO.
Fig. 3
Optimization of the extraction condition
In order to achieve the satisfactory extraction performance of the developed method, different parameters affecting the extraction conditions such as pH, sorbent dose, breakthrough volume, type and volume of eluent, adsorption and desorption times were optimized.
Effect of solution pH
The solution pH can be critical to obtain high yields of the Sm (III) adsorption on the surface of nanosorbent. The proton concentration is a key factor governing the hydrolysis of trivalent lanthanides [8]. So, the binding of the trivalent lanthanides by the carboxylated ligands is strongly pH dependent. pH can influence the state of analyte and the accessibility of binding sites. Hence, the effect of pH on the extraction recovery of Sm (III) ions was evaluated within the range of 3–12. The predominant ionic species of Sm is Sm3+ at pH < 6, whereas the insoluble Sm(OH)3 is formed at pH > 7.5 and become predominant at pH > 11.5 [17]. Under very acidic conditions, a decrease in recovery was observed, probably due to the protonation of PDA and occupation of active sites by protons rather than analyte ions. Therefore, pH 6.0 was selected as the optimal value in subsequent experiments (Fig. 4).
Fig. 4
Effect of sorbent dose
The amount of sorbent plays an important role in the SPE procedure and affects the extraction efficiency. To investigate the effect of this parameter on the recovery of Sm ions, the amount of PDA modified Fe3O4/GO was varied in the range of 10–80 mg. As shown in Fig. 5, the recovery of 50 μg L−1 of analyte ions reaches a maximum value when using 60 mg of sorbent.
Fig. 5
Breakthrough volume
To achieve a higher enrichment factor, the samples with large volume should be transferred into smaller volume via SPE. So, the maximum applicable sample volume was determined by increasing the dilution of solution in range of 25–150 mL, while the total amount of analyte was remained constant. The quantitative recovery for Sm was found to be stable until 100 mL and a decrease was observed with further increase in sample volume. Therefore, the enrichment factor of analyte can be extended by increasing the sample volume up to 100 mL.
Effect of elution conditions
The SPE procedure recovery significantly can be improved by efficient selection of a suitable eluent. In fact, the solvent has a significant effect on the desorption process of the retained ions from the solid phase. Under strong acid conditions, the coordination interaction of chelated Sm (III) ions can be easily disrupted and, subsequently, ions release into the eluent medium. For this purpose, different eluents such as EDTA, HNO3, HCl, CH3COOH and a mixture of HNO3-HCl-CH3COOH were used. As seen in Fig. 6, a recovery of 98.3% was obtained for Sm (III) when eluted with a highly pure acid mixture of HNO3-HCl-CH3COOH (40: 30: 30 % v/v).
Eluent volume in solid phase extraction is important to achieve high enrichment factor. Minimum volume of eluent for quantitative recoveries of adsorbed elements in this procedure was found 800 µL. Thus 800 µL of eluent was used in all further experiments.
Fig. 6
Adsorption and desorption times
The extraction and back extraction experiments were carried out in time intervals of 5–25 and 5–15 min, respectively. At the beginning of the adsorption process, the recoveries increased rapidly by increasing time from 5 to 20 min. After this time, no substantial increase was obtained with longer adsorption time. So, based on these results, 20 min was chosen as the optimal adsorption time. Meanwhile, the experimental results indicated that 12 min is sufficient for quantitative desorption of elements by 800 µL of highly pure acid mixture.
Effect of foreign ions
In order to assess the application of the recommended procedure, the effect of potentially interfering ions on the extraction recovery of Sm (III) was also examined. Foreign ions in different interference-to-analyte ratios were added individually to 100 mL of solutions containing 50 μg L−1 of the analyte, followed by applying the method discussed earlier. As shown in Table 1, the interfering ions have no significant effects on the preconcentration of Sm (III) ions under the mentioned optimum conditions. The obtained results can be attributed to the high affinity of PDA ligand towards Sm ions.
Table 1
Analytical figures of merit
The described extraction method was validated in terms of linearity, limit of detection (LOD), repeatability, reproducibility and enrichment factor. The calibration curve for Sm was linear in the concentration range 6.2-784.5 µg L-1 with a correlation coefficient value greater than 0.9900. The LOD and LOQ for Sm based on 3Sb/m and 10Sb/m (where m is the slope of the calibration curve and Sb is the standard deviation for five blank measurements) were 1.4 and 4.6 µg L-1, respectively. The relative standard deviations (RSDs) for single-sorbent repeatability and sorbent-to-sorbent reproducibility were 5.9% and 8.7% (n=5), respectively. The enrichment factor, calculated by dividing the initial volume of sample solution to the final volume of preconcentrated solution for all elements was 125.
Real sample analysis
To evaluate the applicability of the developed method, spiking water samples were carried out using the standard addition technique, and the results are shown in Table 2. The samples including sea water and river water were tested before addition of Sm (III) standard with the optimised approach and also after its addition. In fact, the samples are analyzed with and without the spike to test recovery. The recovery of the added standards was calculated according to the described protocol. Good correlation was achieved between the added and measured amounts. Generally, the recoveries of Sm (III) ions obtained were in the range of between 97.2% and 109.3%. It should be noted that the evaluation of Sm (III) in sea water as a complex saline matrix at ultra-trace levels has always been a hard task, due to spectral interferences and matrix effects for powerful techniques such as ICP-OES. Thus, the design of a novel method for separation of the matrix components and preconcentration of the analyte procedures is of critical importance.
Table 2
Conclusion
The current study presents a simple approach for synthesis of an effective nanosorbent, in which Fe3O4/GO nanocomposite was noncovalently functionalized with PDA through π-π interactions. Then, we assessed the potential of the PDA ligand for the extraction of Sm (III) from aqueous solutions by using a combination of ICP-OES and recovery studies. It was found that PDA is highly preorganized for samarium complexation and tends to coordinate to Sm3+. An important result from our studies is that the developed nanosorbent has several advantages over the traditional sorbents. With using of PDA ligand, we showed that the interference effects could be overcome. In addition, easy separation of the magnetic sorbent from matrix solution by the application of an external magnet, low consumption of sorbent (60 mg), high recovery (>%97) and low LOD (1.4 μg L−1) are other obvious advantages compared to the alternative sorbents. In conclusion, the high extraction efficiency without interference effects shows that the proposed design improves performance throughout the doping of Fe3O4 nanoparticles into graphene oxide nanosheets as well as modification with a carboxyl-containing ligand.
Acknowledgements
We greatly appreciate the support of this work by Research Councils of Nuclear Science and Technology Research Institute.
References
1. Y. Zhang, C. Zhong, Q. Zhang, B. Chen, M. He, B. Hu, RSC Adv., 5 (2015) 5996–6005.
2. S. Bourg, C. Poinssot, Prog. Nucl. Energy, 94 (2017) 222–228.
3. Sartor O, Rev. Urol., 6 (2004) 3–12.
4. M. Shamsipur, L. Farzin, M.A. Tabrizi, S. Sheibani, Mater. Sci. Eng. C., 77 (2017) 459–469.
5. L. Hadjittofi, S. Charalambous, I. Pashalidis, J. Rare Earth, 34 (2016) 99–104.
6. R.C. Oliveira, C. Jouannin, E. Guibal, Garcia Jr O., Process Biochem., 46 (2011) 736–744.
7. S. Shrvani-Arani, S.J. Ahmadi, A. Bahrami-Samani, M. Gannadi-Maragheh, Anal. Chim. Acta, 623 (2008) 82–88.
8. T. Kiliari, I. Pashalidis, J. Radioanal. Nucl. Chem., 299 (2014) 721–724.
9. F.N. Behdani, A.T. Rafsanjani, M. Korean J. Chem. Eng., 30 (2013) 448–455
10. L. Farzin, M. Shamsipur, S. Sheibani, Microchim. Acta, 183 (2016) 2623–2631.
11. N. Jalilian, H. Ebrahimzadeh, A.A. Asgharinezhad, K. Molaei, Microchim. Acta, 184 (2017) 2191–2200.
12. F. Xie, T.A. Zhang, D. Dreisinger, F. Doyle, Miner Eng., 56 (2014) 10–28.
13. R. Safarbali, M.R. Yaftian, A. Zamani, J. Rare Earth, 34 (2016) 91–98.
14. M.E. Azenha, H.D. Burrows, S.M. Fonseca, M.L. Ramos, J. Rovisco, J.S. De Melo, A.J.F.N. Sobral, K. Kogej, New J. Chem., 32 (2008) 1531–1535.
15. J.J. Zhang, N. Ren, Y.X. Wang, S.L. Xu, R.F. Wang, S.P. Wang, J. Braz. Chem. Soc., 17 (2006) 1355–1359.
16. L. Farzin, M. Shamsipur, M. Shanehsaz, S. Sheibani, Int. J. Environ. Anal. Chem., 97 (2017) 854–867.
17. M.R. Mahmoud, M.A. Soliman, K.F. Allan, Radiochim. Acta, 103 (2014) 443–456.