Investigation of Adhesion Behavior of Aluminum Laminates /Carbon Fiber/ High Silica Fiber by Phenol Resins

محورهای موضوعی : composite materials

kazem Salimi ¹ , Alireza Naddaf Oskouei ² , Rouhollah Hosseini ³ , Mohammad Javad Zeinalbeik ⁴

1 - UniversityDepartment of Mechanical Engineering Imam Hossein Comprehensive University, Tehran, Iran of Imam Hossein
2 - Department of Mechanical Engineering Imam Hossein Comprehensive University, Tehran, Iran
3 - Department of Mechanical Engineering Imam Hossein Comprehensive University, Tehran, Iran
4 - Department of Mechanical Engineering Imam Hossein Comprehensive University, Tehran, Iran

تاریخ دریافت : 1401/06/05 تاریخ پذیرش : 1401/10/28 تاریخ انتشار : 1402/06/10

کلید واژه: high silica, phenol resins, Strength, Carbon,

چکیده مقاله :

Fiber‐metal laminate is a material constituted of composite laminate and metal sheets, whose mechanical properties can be tailored by varying the thickness, the number of layers and bonding type. For this reason, in this research, strength test, adhesion test and flux test for a sandblasted and etched aluminum sheet that contained a seven-layer composite with 2 types of adhesion treatment (phenol adhesive/resin of composite material) and front side composite layup (High-silica/High-silica+Carbon) were investigated. It was found that the above-mentioned factors influenced the flexural strength of FML; precisely, the presence of an adhesive layer between the composite plies and the metal sheet made the flexural strength decrease, while this mechanical parameter increased passing from two metal sheets to only one. The results show that the presence of carbon layer has led to the greatest increase in strength due to strong bonding. Also, the results of the flux test show that the behavior of the two samples is very close to each other.

منابع و مأخذ:

• Xu, R., Huang, Y., Lin, Y., Bai, B., and Huang, T., In‐Plane Flexural Behaviour and Failure Prediction of Carbon Fibre‐Reinforced Aluminium Lami-Nates, J Reinf Plast Compos, Vol. 36, 2017, pp. 1384‐1399.


• Rajkumar, G. R., Krishna, M., Narasimhamurthy, H. N., Keshavamurthy, Y. C., and Nataraj, J. R., Investigation of Tensile and Bending Behavior of Alu-Minum Based Hybrid Fiber Metal Laminates, Procedia Mater Sci., Vol. 5, 2014, pp. 60‐68.


• Botelho, E. C., Silva, R. A., Pardini, L. C., and Rezende, M. C., A Review on The Development and Properties of Continuous Fiber/Epoxy/Aluminum Hybridcomposites for Aircraft Structures, Mater Res., Vol. 9, 2006, pp. 247‐526.


• Kim, J. G., Kim, H. C., Kwon, J. B., Shin, D. K., Lee, J. J., and Huh, H., Tensile Behavior of Aluminum/Carbon Fiber Reinforced Polymer Hybrid Composites Atintermediate Strain Rates, J Compos Mater., Vol. 49, 2015, pp. 1179‐1193.


• Şen, I., Alderliesten, R. C., Benedictus, Lay‐up Optimisation of Fibre Metal Laminates Based on Fatigue Crack Propagation and Residual strength, Compos Struct, Vol. 124, 2015, pp. 77‐87.


• Bellini, C., Polini, W., and Sorrentino, L., A New Class of Thin Composite Parts for Small Batch Productions, Adv Compos Lett., Vol. 23, 2014, pp. 115‐120.


• Hu, Y. B., Li, H. G., Cai, L., and et al., Preparation and Properties of Fibre‐Metal Laminates Based on Carbon Fibre Reinforced PMR polyimide, Compos Part B Eng., Vol. 69, 2015, pp. 587‐591.


• Dhaliwal, G. S., Newaz, G. M., Experimental and Numerical Investigation of Flexural Behavior of Carbon Fiber Reinforced Aluminum Laminates, J Reinf Plast Compos., Vol. 35, 2016, pp. 945‐956.


• Bellini, C., Di Cocco, V., Iacoviello, F., and Sorrentino, L., Experimental Analysis of Aluminium Carbon/Epoxy Hybrid Laminates Under Flexural Load, Frattura ed Integrità Strutturale., Vol. 48, 2019.


• Pan, L., Ali, A., Wang, Y., Zheng, Z., and Lv, Y., Characterization of Effects of Heat-Treated Anodized Film on The Properties of Hygrothermally Aged AA5083‐Based Fiber‐Metal Laminates, Compos Struct, Vol. 167, 2017, pp. 112‐122.


• Rajan, B. M. C., Kumar, A. S., The Influence of The Thickness and Areal Density on The Mechanical Properties of Carbon Fibre Reinforced Alumin-Ium Laminates (CARAL), Trans Indian Inst Met., Vol. 71, 2018, pp. 2165‐2171.


• Li, H., Hu, Y., Fu, X., Zheng, X., Liu, H., and Tao, J., Effect of Adhesive Quantity on Failure Behavior and Mechanical Properties of Fiber Metal Lam-Inates Based on The Aluminum‐Lithium Alloy. Compos Struct., Vol. 152, 2016, pp. 687‐692.


• Shuang Wang, H. H., Ye, T., and Jie. H., Effects of SiC Content on Mechanical, Thermal and Ablative Properties of Carbon/Phenolic Composites, Ceramics International, 2020.


• Shuang Wang, H. H., Ye, T., Effects of Zirconium Carbide Content on Thermal Stability and Ablation Properties of Carbon/Phenolic Composites, Ceramics International, 2019.


• Heydari Vini, M., Daneshmand, and S., Jahangiri Sadri, A., The Investigation of the Corrosion Resistance of Al/Alumina Composites Fabricated Via ARB Process. New Process in Material Engineering, 2022, Vol. 16, No. 3, pp. 43-54.


• Heydari Vini, M., Daneshmand. S., Mechanical and Bonding Properties of Bi-Metal Al/Cu Bulk Composites Produced Via ABP Technique, Surface Review and Letters, Vol. 28, NO. 11, 2021.


• Heydari Vini, M., Daneshmand. S., Mechanical and Wear Properties Evaluation of Al/Al2O3 Composites Fabricated by Combined Compo-Casting and WARB Process, Advances in Computational Design, Vol. 7, No. 2, pp. 129-137.


• Abdalkareem Jasim, S., Heydari Vini, M., and Daneshmand, S., Bonding Properties of Al/Al₂o₃ Bulk Composites Produced Via Combined Stir Casting and Accumulative Press Bonding. Surface Review and Letters, Vol. 29, No. 04, 2022.


• Zahedinia, M., Hosseini, R., Khodarahmi, H., and Ziashamami, M., Experimental and Numerical Study of Deformation of FML Plates with the Same Thickness Under Explosive Loading, Journal of Solid and Fluid Mechanics, Vol. 8, No. 4, pp. 129-142.


• Kiani, A., Hosseini, R., and Khodarahmi, H., Non-Linear Response of Fiber Metal Laminates Subjected to Dynamic Loading, In Persian, Journal of Science and Technology of Composites, Vol. 7, No. 1, 2020, pp. 768-778.


• Kiani, A., Hosseini, R., Khodarahmi, H., Investigation of Transient Nonlinear Response of Fiber Metal Laminates (fml’s) under Uniform Time-Dependent Pressure Loading, Journal of Aerospace Mechanics, Vol. 18, No. 3, 2022, pp. 109-125.


• Khondabi, R., Khodarahmi, H., Hosseini, R., and Zia Shamami, M., Experimental and Numerical Investigation on Performance of Sandwich Panels Using Aluminum Faces and Polyurethane Foam Core with Variable Density Against Explosive Loading, Iranian Mechanical Engineering Research Journal, Vol. 22. No. 1, 2020.


• Khondabi, R., Khodarahmi, H., Hosseini, R., and Zia Shamami, M., Experimental and Numerical Investigation into the Effect of Core Density on the Energy Absorption of Sandwich Panels with Aluminum Face Sheets and Polyurethane Foam Core. Amirkabir J. Mech. Eng., Vol. 52, No. 10, 2021, pp. 705-708.


• Khondabi, R., Khodarahmi, H., Hosseini, R., and Zia Shamami, M., Experimental and Numerical Study of Core and Face-Sheet Thickness Effects in Sandwich Panels with Foam Core and Aluminum Face-Sheets Subjected to Blast Loading, Journal of Solid and Fluid Mechanics, Vol. 8, No. 3, pp. 91-106.


• Hatampour, M., Hosseini, R., Hasanzadeh, M., and Vahedi, K. H., Experimental Investigation and Regression Analysis on Plastic Deformation of Sandwich Panels Made of Reinforced Polymeric Foam under Explosive Loading, Modares Mechanical Engineering, Vol. 20, No. 11, 2020, pp. 2671-2678.


• Hoseini, R., Elhami, M. R., Mansouri Lotfali, S., Marashi, S., The Width Reduction Effect of a Piezoelectric Energy Harvesting Composite Beam on Output Power: An Experimental and Analytical Study, Journal of Aerospace Mechanics, Vol. 17, No. 3, 2021, pp. 71-83.