  • A study on the sub-structure and mechanical properties of friction stir processed AA 6061-T6 joints with ultra-fine grained structure

اشتراک گذاری

آدرس مقاله


کد مقاله : 1009-JMATPRO (R2) بازدید : 103 صفحه: 33 - 46

نوع مقاله: پژوهشی

A study on the sub-structure and mechanical properties of friction stir processed AA 6061-T6 joints with ultra-fine grained structure

محورهای موضوعی : Welding

Ali Salemi Golezani 1 , M. Esmaily 2 , N. Mortazavi 3

1 - Department of Materials Engineering, Karaj Branch, Islamic Azad University, Karaj, Iran.
2 - Department of Chemical and Biological Engineering, Chalmers University of Technology, Göteborg, Sweden.
3 - Department of Applied Physics, Chalmers University of Technology, Göteborg, Sweden.

تاریخ دریافت : 1392/08/26 تاریخ پذیرش : 1392/10/21 تاریخ انتشار : 1392/11/12

کلید واژه: Friction stir wrocessing, Aluminum Alloy, sub-structural analysis, dislocation density,

چکیده مقاله :

Ultra-fine grained (UFG) structure (~0.6 µm) was produced in the stir zone (SZ) of 6061-T6 aluminum alloy joints using friction stir processing (FSP) cooled by liquid nitrogen (N2). A new experimental set-up was used to simultaneously quench the lower and upper surfaces of the samples during the processing. In addition, FSPed joints, using a steel backing plate, were produced at room temperature as a reference. Sub-structural studies have been carried out to investigate the occurrence of dynamic recrystallization and grain growth in the weld area of the samples. The results indicate that the microstructure was not fully recrystallized as a high dislocation density (3.5×1014 m-2) was measured in the stir zone (SZ) of rapidly cooled joints in compare with that of the air-cooled joints (1.5×1014 m-2). Moreover, the rapid cooling generated a very high dislocation density of about 6.5×1014 m-2 in the thermo-mechanical affected zone (TMAZ). Accordingly, better mechanical properties were obtained in the SZ. In contrast, lower strain hardening capacity and hardening exponent values were obtained in the rapidly cooled joints where the highest fraction of low angle grain boundaries (LAGBs) and largest number of dislocations were measured.

چکیده انگلیسی:

منابع و مأخذ:

 

  1. H. Hasegawa, S. Komura, A. Utsunomiya, Z. Horita, M. Furukawa, M. Nemoto M, Mater. Sci.Eng.A. 265, 1999, pp. 188-196.
    2.
  2. R. Z. Valiev, R. K. Islamgaliev, I.V. Alexandrov, Prog. Mater. Sci. 45, 2000,
    pp. 103-189.
    3.
  3. M. Umemoto, T. Todaka, J.L. Tsuchiya, Mater. Sci. Forum. 503, 2006, p. 11-8.
    4.
  4. C. M. Hu, C. M. Lai, P. W. Kao, N. J. Ho, J. C. Huang, Mater. Chara. 61, 2010,
    pp. 1043-1053.
    5.
  5. N. Kumar, R.S. Mishra, Mater. Chara. 74, 2012, pp. 1-10.
    6.
  6. K. T. Park, H. J. Kwon, W. J. Kim, Y. S. Kim, Mater. Sci. Eng.A. 316, 2001,
    pp. 145-152.
    7.
  7. Y. J. Kwon,I.Shigematsu, N. Saito, Mater. Trans. 45, 2004, pp. 2304-2311.
    8.
  8. D. Orlov, Y. Todaka, M. Umemoto, Y. Beygelzimer, Z. Horita, N. Tsuji, Mater. Sci. Forum 604, 2009, pp. 171-178.
    9.
  9. H. Alihosseini, G. Faraji, A.F. Dizaji, K. Dehghani, Mater. Chara. 68, 2012, pp. 14-21.
    10.
  10. R. S. Mishra, M. W. Mahoney, S. X. McFadden, N. A. Mara, A. K. Mukherjee, Scr. Mater. 42, 2000, pp. 163-168.
    11.
  11. R. S. Mishra, M. W. Mahoney, Mater. Sci. Forum. 507, 2001, pp. 357-359.
    12.
  12. Z. Y. Ma, R. S. Mishra, M. W. Mahoney, Acta Mater. 50, 2002, pp. 4419-4430.
    13.
  13. A. H. Feng, Z. Y. Ma, Scr. Mater. 56, 2007, pp. 397-400.
    14.
  14. Y. Morisada, H. Fujii, T. Nagaoka, M. Fukusumi, Mater. Sci.Eng.A. 419, 2006, pp. 344-348.
    15.
  15. J.-Q Su, T. W. Nelson, C. J. Sterling, J. Mater. Res. 18, 2003, pp. 1757-1760.
    16.
  16. C. G. Rhodes, M. W. Mahoney, W. H. Bingel, M. Calabrese, Scr. Mater. 48, 2003, pp. 1451-1455.
    17.
  17. Z. Y. Ma, R. S. Mishra, M. W. Mahoney, R. Grimes, Mater. Sci. Eng.A. 351, 2003,
    pp. 148-153.
    18.
  18. I. Charit, Z. Y. Ma, R. S. Mishra, In: Taleff EM, Friedman PA,KrajewskiPE, Mishra RS, Scroth JG, editors. Warrendale (PA), TMS, 2004.
    19.
  19. M. Esmaily, A. Shokuhfar, Def. Diff. Forum 297, 2010, pp. 1116-1121.
    20.
  20. W. Woo, H. Choo, D. W. Brown, Z. Feng, Metal. Mater. Trans. A. 38A, 2007, pp. 69-76.
    21.
  21. M. El-Rayesa, E. A. El-Danafa, J. Mater. Proc. Technol. 212, 2012, pp. 1157-1168.
    22.
  22. K. Elangovan, V. Balasubramanian, Mater. Desig. 29, 2008, pp. 362-373.
    23.
  23. W. Woo, H. Choo, D. W. Brown, Z. Feng, P. K. Liaw, Mater. Sci.Eng.A. 437, 2006, pp. 64–69.
    24.
  24. W. Woo, Z. Feng, X.-L. Wang, D.W. Brown, B. Clausen, K. An, H. Choo, C.R. Hubbard, S.A. David, Sci. Technol. Weld. Join. 12, 2007, pp. 298–303.
    25.
  25. C. I. Chang, X. H. Du, J. C. Huang, Scr. Mater. 57, 2007, pp. 209-212.
    26.
  26. K. Poorhaydari, B. M. Patchett, D. J. Ivey, Weld. J. 48, 2005, pp. 149S-155S.
    27.
  27. P. Suortti. The Rietveld Method, R.A. Young (Ed.).OxfordUniversityPress,Oxford, IUCr Monographs on Crystallography. pp. 167-185.
    28.
  28. M. A. Krivoglaz. Theory of X-ray and Thermal Neutron Scattering by realCrystals. Plenum Press,New York, pp. 1969:258.
    29.
  29. T. Ungar, H. Mughrabi, D. Ronnpagel, M. Wilkens, Acta Metall. 32, 1984, pp. 333-342.
    30.
  30. A. Sarkar, A. Bhowmik, S. Suwas, Mater. Sci. Proc. 94, 2009, pp. 943–948.
    31.
  31. A. Sarkar, P. Mukherjee, P. Barat, Mater. Sci. Eng. A. 485, 2008, pp. 176–181.
    32.
  32. W. Woo, T. Ungar, Z. Feng, E. Kenik, B. Clausen, Metall. Trans. A. 41, 2010,
    pp. 1210-1216.
    33.
  33. M. W. Mahoney, R. S. Mishra, ASM International. 2007, p. 42.
    34.
  34. G. G. Roy, R. Nandan, T. DebRoy, Sci. Tech. Weld. Join. 11, 2006, pp. 606-608.
    35.
  35. M. Esmaily, S. N. Mortazavi, P. Todehfalah, M. Rashidi, Mater. Desig. 47, 2013,
    pp. 143-150.
    36.
  36. K. Lu, M.L. Sui, Scr. Mater. 28, 1993, pp. 1465-1470.
    37.
  37. W. Zhang, H. Wang, R.W. Scattergood, J. Narayan, C.C. Koch, Acta Mater. 50, 2002, pp. 3995-4004.
    38.
  38. T. W. Nelson, J. Q. Su, R. Mishra, M. Mahoney, Acta Mater. 51, 2003, pp. 713-729.
    39.
  39. G. Liu, L.E. Murr, C.S. Niou, J.C. McClure, F.R. Vega, Scr. Mater. 37, 1997, pp. 355-361.
    40.
  40. S. Lim, S. Kim, C.G. Lee, S.J. Kim, Metall. Mater. Trans. A. 35, 2004, pp. 2829-2835.
    41.
  41. S. R. Ren, Z. Y. Ma, L. Q. Chen, Scr. Mater. 56, 2007, pp. 69-72.
    42.
  42. A. Scialpi, L. A. DeFilippis, P. Cavaliere, Mater. Desig. 28, 2007, pp. 1124-1129.
    43.
  43. P. A. Manohar, D. P. Dunne, T. Chandra, C. R. Killmore, ISIJ Int., 36, 1996, pp. 194-196.
    44.
  44. W. Read, W. Shockley, Phys. Rev. 78, 1950, pp. 275-289.
    45.
  45. M. Taheri, H. Weiland, A. Rollett, Metall. Mater. Trans. A. 37, 2006, pp. 19-25.
    46.
  46. M. Cabibbo, E. Meccia, E. Evangelista, Mater. Chem. Phys. 81, 2003, pp. 289-292.
    47.
  47. R. W. Fonda, J. F. Bingert, Metall. Mater. Trans. A. 35, 2004, pp. 1487-1499.
    48.
  48. S. H. Kang, W. H. Bang, J. Cho, H. Han, H.H. Oh, C.G. Lee, S.J. Kim, Mater. Sci. Forum 905, 2005, pp. 495-497.
    49.
  49. C. Hamilton, S. Dymek, M. Blicharski, W. Brzegowy, Sci. Tech. Weld. Join. 12, 2007, pp. 702-707.
    50.
  50. J. Luo, Z. Mei, W. Tian, Z. Wang, Mater. Sci.Eng.A. 441, 2006, pp. 282–290.
    51.
  51. N. Afrin, D. L. Chen, X. Cao, M. Jahazi, Scr. Mater. 57, 2007, pp. 1004-1007.
    52.
  52. G. E. Dieter, Mechanical Metallurgy,McGraw-Hill,New York, Third edition, 1986.
    53.
  53. W. F. Hosford, Mechanical Behavior of Materials,CambridgeUniversityPress,New York, 2005.
    54.
  54. M. J. Starink, A. Deschamps, S. C. Wang, Scr. Mater. 58, 2008, pp. 377–382.
    55.
  55. Y. S. Sato, H. Kokawa, M. Enomoto, S. Jogan, Metall. Trans. A. 30,1999, pp. 2427-37.
    56.
  56. B. Heinz, B. Skrotzki, Metall. Mater. Trans. B. 33, 2002, pp. 489-498.
    57.
  57. C. Gallais, A. Denquin, Y. Brechet, G. Lapasset, Mater. Sci. Eng.A. 496, 2008,
    pp. 77-89.
    58.

سکوی نشر دانش

سند یا سکوی نشر دانش ،سامانه ای جهت مدیریت حوزه علمی و پژوهشی نشریات دانشگاه آزاد می باشد

پیوندهای سایت

مراکز مرتبط

پشتیبانی

صفحات رسمی

حقوق این وب‌سایت متعلق به سامانه مدیریت نشریات دانشگاه آزاد اسلامی است.
حق نشر © 1403-1400

صفحه اصلی| عضویت/ ورود| درباره سند| تماس با ما|
[English] [العربية] [en] [ar]