In the present study, silver-doped TiO2 (Ag/TiO2) nanoparticles were prepared by various Ag doping (wt%) and a combination of sol-gel and ultrasound irradiation. Ag/TiO2 nanoparticles were characterized by energy-dispersive X-ray analysis (EDX), scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques. Based on the Taguchi method, photocatalytic degradation of (Reactive Blue 255) RB 255 azo dye was examined with Ag/TiO2 nanoparticles under visible light irradiation. Using this method, operation factors such as Ag doping (wt%), pH, mass of catalyst (g) and RB 255 concentration (ppm) were optimized successfully. The results showed that pH, compared to the other factors, plays an important role in the photocatalytic degradation of RB 255 azo dye. The isotherm study Weber-Van Vliet and Fritz-Schlunder (IV) models are the best descriptors of equilibrium behavior. In addition, the kinetic study results indicated that the pseudo first-order has a good agreement with the experimental data. Manuscript profile

در این پژوهش، نانوذرات مس (I) اکسید با استفاده از مس استات به‌عنوان پیش ساز به روش فوق اشباع سنتز شد. به‌منظور افزایش ویژگی فوتوکاتالیستی Au بر روی نانوذرات Cu2O به روش تلقیح مرطوب بارگذاری شد و با استفاده از روش‌های پراش پرتو XRD) X)، میکروسکوپ الکترونی روبشی (SEM) و تجزیه عنصری به روش EDX مورد مشخصه یابی قرار گرفت. تخریب فوتوکاتالیستی رنگ آزویی Direct Red 264 با نانوذرات Cu2O و Au بارگذاری شده بر روی Cu2O تحت تابش نور مرئی و بدون تابش نور مرئی موردبررسی قرار گرفت. بازده تخریب فوتوکاتالیستی با کاتالیست‌های یادشده تحت تابش نور مرئی به ترتیب برابر با 71/63 و 18/96% به‌دست آمد. مطالعات ایزوترمیک تخریب فوتوکاتالیستی توسط این کاتالیست‌ها موردبررسی قرار گرفت. هم‌دماهای فریتز شلاندر 4 پارامتری و بادو به‌عنوان بهترین مدل با ضریب همبستگی 9960/0 و 9988/0 و کمترین میزان خطا به ترتیب برای نانوذرات Cu2O و Au بارگذاری شده بر روی Cu2O انتخاب شد. Manuscript profile