مقاله
1 - Application of mesoporous silica containing benzotriazole in the epoxy coating applied to plain carbon steel and study of its corrosion behaviorJournal of Advanced Materials and Processing , شماره 4 , سال 6 , تابستان 2018The idea of smart inhibitors is based on the principle that an inhibitor is used where needed. This will reduce the use of inhibitors and protect materials in hostile environments. On the other hand, direct addition of the inhibitor within the coating can be harmful, re چکیده کاملThe idea of smart inhibitors is based on the principle that an inhibitor is used where needed. This will reduce the use of inhibitors and protect materials in hostile environments. On the other hand, direct addition of the inhibitor within the coating can be harmful, resulting in the loss of inhibitors ability, deterioration in the coating or both of them. An appropriate method for solving these problems is the use of neutral host systems that act as a nanocontainer system or reservoir and are filled with arbitrary inhibitor. In this study, mesoporous silica with and without corrosion inhibitor (benzotriazole) were dispersed within an epoxy coating to protect the steel sheet. Then, the corrosion properties of these coatings with and without mesoporous silica particles were compared in a saline solution. Electrochemical studies showed that coatings containing particles could protect the surface of steel in the chloride environment. The impedance modulus (Z100 mHz) and corrosion resistance (Rcorr) regarding the coating embedded with mesoporous silica doped with inhibitor showed a value about one order of magnitude higher than that of a coating without inhibitor. This behavior could be due to the release of benzotriazole at the interface of the epoxy coating. In addition, the scratched coating with mesoporous silica doped with inhibitor exhibited less corrosion products compared to the coating without inhibitor which also confirmed the release of benzotriazole on demand of the corrosion process. پرونده مقاله -
مقاله
2 - Addition of Mo in the Zn based alloy coating in the citrate solution and investigation of its corrosion behaviorJournal of Advanced Materials and Processing , شماره 1 , سال 7 , زمستان 2019In this work, Zn-Co-Mo coatings were electrodeposited on mild steel substrate from a citrate solution at current densities of 5, 7.5 and 10 mA.cm-2 and pH values of 4.5, 5, and 5.5. The coated samples were studied by scanning electron microscope and potentiodynamic pola چکیده کاملIn this work, Zn-Co-Mo coatings were electrodeposited on mild steel substrate from a citrate solution at current densities of 5, 7.5 and 10 mA.cm-2 and pH values of 4.5, 5, and 5.5. The coated samples were studied by scanning electron microscope and potentiodynamic polarization. The corrosion behavior of the coatings was related to the molybdenum content and formation of local anodes and cathodes. According to the results, a distinct range of current and pH was recognized to provide high quality and corrosion resistant coatings. The percentage of molybdenum as an alloying element plays an important role in the improvement of the corrosion properties of the coating. The formed coating at pH of 5.5 with 13 wt. % Mo showed the lowest corrosion current density with a value of 0.5 µA.cm-2.The molybdenum coating also showed a passive-like behavior in the anodic region due to the presence of molybdenum in the coating composition. پرونده مقاله -
مقاله
3 - بررسی خواص سایشی آلیاژ آلومینیم 6061 و کامپوزیت حاوی نانولولههای کربنی ساختهشده به روش آلیاژسازی مکانیکی و فرایند پرس داغفصلنامه علمی - پژوهشی مواد نوین , شماره 4 , سال 9 , پاییز 1397در این پژوهش آلیاژ آلومینیم نانوساختار و کامپوزیتهای پایه آلومینیمی حاوی مقادیر مختلف نانولولههای کربنی ( wt.%5/1-5/0) به روش ترکیبی آلیاژسازی مکانیکی و پرس داغ تولید گردید. آزمایشها نشان داد که افزودن نانولوله کربنی تا 1 درصد وزنی به میزان جزئی دانسیته نسبی کامپوزیت چکیده کاملدر این پژوهش آلیاژ آلومینیم نانوساختار و کامپوزیتهای پایه آلومینیمی حاوی مقادیر مختلف نانولولههای کربنی ( wt.%5/1-5/0) به روش ترکیبی آلیاژسازی مکانیکی و پرس داغ تولید گردید. آزمایشها نشان داد که افزودن نانولوله کربنی تا 1 درصد وزنی به میزان جزئی دانسیته نسبی کامپوزیت آلومینیم – نانولوله کربنی را افزایش میدهد. این در حالی است که مقادیر سختی کامپوزیت فوق با افزایش نانولولههای کربنی به دلیل قرارگیری نانولولههای کربنی در فضای خالی بین ذرات پودر و پر شدن میکرو حفرات بهطور قابلملاحظهای افزایشیافته است. مقدار سختی از HV 3/93 مربوط به آلومینیم درشت دانه به HV 18/219 رسید. مقادیر بیشتر نانولولههای کربنی موجب کاهش سختی و دانسیته نسبی کامپوزیت تولیدی گردید. رفتار سایشی کامپوزیتهای آلومینیومی حاوی نانولولههای کربنی به روش پین روی دیسک موردبررسی قرار گرفت. نتایج نشان داد که اضافه کردن نانولولههای کربنی تا میزان 1 درصد وزنی به کامپوزیت موجب کاهش ضریب اصطکاک و کاهش وزن گردیده است. مقدار ضریب اصطکاک آلومینیم درشت دانه در محدوده (91/0-33/0) و برای نمونه حاوی 1 درصد وزنی، ضریب اصطکاک حالت پایدار در محدوده (45/0-42/0) تغییر کرد. همچنین کاهش وزن نیز از 1/44 به 4/7 میلیگرم رسید. این در حالی است که افزایش مقادیر بیش از آن به دلیل ایجاد پدیده تودهای شدن موجب افزایش ضریب اصطکاک و کاهش وزن کامپوزیت آلومینیمی میگردد. نتایج آزمونهای سایش برای آلومینیوم درشتدانه، نانوساختار و کامپوزیت آلومینیم حاوی 1 درصد وزنی نانولوله کربنی نشان داد که مکانیزم سایش به ترتیب چسبان، ورقه ورقه شدن و خراشان است. پرونده مقاله